回复 160# limeihua20 的帖子
Chilled cast iron = white cast iron有些是英國書上的相片
[ 本帖最后由 leomet 于 2009-7-29 19:01 编辑 ]
AISI 4340
Casting鑄件樹枝狀偏析SNCM 440; 40NiCrMo?
Quenched and tempered.
Please note the dendritic segregation.
Photo ~1781: dendrite arm boundary (2) is solute-rich, rich in C and alloying elements. You will often find carbide particles and R.A. on these spots.
[ 本帖最后由 leomet 于 2009-7-25 15:18 编辑 ] 本帖最后由 leomet 于 2009-12-9 07:47 编辑
另一組相片
同上 same as above光奌是 points last to freeze. 枝晶最後凝固奌.
20多年了, 最近才突然想到: 我應該是台灣第一個拍彩色金相的---since 1984.1980年讀台科大研究所時, 影印了圖書館裡彩色金相的洋文書, 德英双語, E. Weck, E. Leistner合著. 1983年在台中金屬中心任金相檢驗工作, 照著書本試試. 這樣, 一不小心就成了台灣第一.通常知道金相為何物者, 不管是當年或現在, 第一次看到時, 都會有一種"驚豔"的感覺.
[ 本帖最后由 leomet 于 2009-8-12 05:33 编辑 ] 吴老师，你发的照片让人赏心悦目啊，让人佩服。能不能再发一些铸态奥氏体不锈钢的金相照片，学习一下，谢谢！
[ 本帖最后由 lansure 于 2009-7-26 19:36 编辑 ]
铸态奥氏体不锈钢
~ AISI 310 耐熱鋼Austenite dendriteswith carbides particles between dendrite arms ( that is, dendrite arm boundary)
that are sites last to freeze.
[ 本帖最后由 leomet 于 2009-7-27 11:36 编辑 ] 本帖最后由 leomet 于 2009-10-25 13:27 编辑
另外一組相片
另外一組相片, 熱處理爐內托盤,[ 本帖最后由 leomet 于 2009-7-30 05:46 编辑 ]
4140
給大家看圖說話.1020 C air-cooled.
[ 本帖最后由 leomet 于 2009-8-8 08:56 编辑 ]
P91材料，怎么腐蚀才能更好的观察碳化物，统计碳化物粒径
P91老化材料，组织为回火马氏体，怎么样腐蚀才能更好的观察组织里面的碳化物，若是做彩色金相用什么侵蚀液请高手您指教QT 铸铁金相 欣赏
JIS : FCD 650 ?Not that bad !
[ 本帖最后由 leomet 于 2009-8-2 07:59 编辑 ]
FT 铸铁金相 欣赏
I am a man of few words, So, no discussion here.I am a man with a thousand photos, and I
hope you guys enjoy seeingthe photos I post.
D-type graphite caused bytoo much undercooling.
Casting probably poured at too low a temperature.
Or, that part of the casting (lug)happened to be fed withfront metal.
[ 本帖最后由 leomet 于 2009-8-1 11:27 编辑 ]
FT 铸铁金相 欣赏
Photos that feast your eyes.FT 铸铁金相 欣赏
Photos that feast your eyes.It will be a pitty not sharing with you. 照片太漂亮了，是否有不锈钢904，2205的照片，上传一下，欣赏欣赏。
回复 155# 盛丽丽 的帖子
不锈钢, the only one I did: AISI 304[ 本帖最后由 leomet 于 2009-8-9 07:34 编辑 ]
回复
老师你好，请问此图材料904，状态固溶，王水腐蚀，个人认为白区是奥氏体，灰色区是铁素体，对否？回复 157# 盛丽丽 的帖子
If yes, it should be the other way around. Delta ferrite is white.My opinion : only austenite phase exists after solution quenching.
I say so because there is no phase boundary.
This segregation is also named as " coring segregation". 漸層.
[ 本帖最后由 leomet 于 2009-8-12 23:47 编辑 ]
共晶碳化物 in 球鉄
Eutectic carbidein the matrix of a 15% Ni ductile iron.Nodularity of graphite is not-so-good.
[ 本帖最后由 leomet 于 2009-8-14 09:04 编辑 ]
Cr12MoV模具钢金相组织
下图为我单位使用的Cr12MoV冷冲模具，热处理后HRC55-57，使用寿命极短，失效形式是断裂，不知道是原材料问题还是热处理问题。[ 本帖最后由 lwjonly 于 2009-8-15 13:11 编辑 ] Very good photo, thank you, Mr wu, I have learnt so muchu from you professional work.